Nylon rod (PA) should use precautions: PA machining and assembly Reference Notes: machining: (1) turning lathe speed not too fast, generally require less than 600 rev / min, feed rate should not be too large Otherwise, the heat caused by expansion of product specifications nylon rod which processing is totally inconsistent with the size. (2) before turning angle should be bigger than the turning of steel, after turning angle larger than the anterior horn, before angle of 15o-25o, after the angle is about 15oC, only general oil the blades can be, without the use of alloy tool. (3) planer processing, not by hand knives, knife application process, after planing angle is smaller, hand knife will cause nylon pieces of smooth crack off the block. (4) application of oil or water when turning saponification. (5) When drilling nylon rod density, with an outer diameter less than or equal to the rod diameter is drilled 1/3 (but not exceeding the maximum drill diameter 25mm), the drill angle take 90-110o, the vehicle speed does not exceed 200 r / min, feed should not be too large, and to promptly withdraw the drill bit to clean nylon chips, after saponification water or oil cooling, according to the above procedure and then continue drilling or reaming, and prevent heat caused by the drill nylon expansion cracking. (Note: The larger the diameter of the rod especially over 100mm diameter rods, drill press but also to regulate the operation) as drilled 20mm hole should be small drill, after gradually expanded to prevent cracking. When the hole to draw oil nest after nest should be zoned drilling, drilling plans if the first nest is easy to make the workpiece with the drill bit float (the term for the tree) and easy bruising processing staff, the waste. Nylon rods used widely, so if you have questions about the production process of nylon rods, nylon rods Why choose it? Today nylon rod factory Zibo New Haven Rubber Co. is to tell you the reason. Nylon rod has good toughness, wear resistance, oil resistance, earthquake, stretching, bending strength, and has low water absorption, good dimensional stability and other characteristics, which are used to process a variety of high-strength wear-resistant parts. This product is versatile, good material is plastic and steel, iron, copper and other metals. And nylon rod are important engineering plastics having a high strength, high stiffness, high impact and notch toughness, heat distortion resistance, high evaporation, high wear resistance of the toughness, good sliding properties, ultimate non-lubricating properties, high chemical stability, resistance to organic solvents and fuel nylon rods, non-toxic, but gentle suction dimensional changes and the mechanical and electrical changes, very good performance. Which cast nylon rods | Texas Wang Yue (certified) | Siping nylon rods provided by Dezhou Hongyue Composites Limited. Dezhou Hongyue Composite Materials Co., Ltd. (www.hyfhcl.com) Shandong Dezhou, chemical products processing leader, over the years, the company is implementing the scientific management, innovation and development, the principle of honesty and trustworthiness, and satisfy customer needs. Wang Yue in Texas led the staff warmly welcome all inquiries negotiations to create the Texas Hongyue a better future.